Reliability prediction in electronic packages using molecular simulation

Authors Fan, H.B. HKUST affiliated (currently or previously)
Wong, C.K.Y. HKUST affiliated (currently or previously)
Yuen, M.M.F. View this author's profile
Issue Date 2005
Source Proceedings - Electronic Components and Technology Conference , v. 2, 2005, p. 1314-1317
Summary Reliability of electronic packages is a great concern to packaging design engineers. During its design life, packages experience a wide range of temperature variations. The mismatch in coefficient of thermal expansion between the different layers in the packages can generate high interfacial stresses due to these thermal loading. If these stresses exceed the limiting value, delamination will occur. The present study is focused on the reliability of the epoxy molding compound (EMC) and cuprous oxide coated copper substrate. In order to verify whether the interfacial adhesion is dominant by the content of cuprous oxide on the cooper substrate, two models were built to simulate the thermal cycling test with a constant cuprous oxide and a changing content of cuprous oxide on the copper substrate. The thermal cycling test was conducted with a given thermal profile. The adhesion strength between EMC and cuprous oxide coated copper substrate at different thermal cycles was evaluated using the button shear test (BST). A simple molecular model of a bi-material system, which consists of EMC and cuprous oxide coated copper substrate, was built to evaluate the interfacial energy of the Cu-EMC system. In order to dramatically reduce the computational time, the system was modeled with a limited number of atoms. A preset strain was applied to the model representing a forcing step as the EMC material was pulled away from the copper substrate. Equilibration was conducted to relax the whole system before the next strain step proceeded. The procedure was repeated using different strains. The interfacial energy at different thermal cycles was evaluated. The variation of the interfacial energy indicated the change in the adhesion strength between EMC and cuprous oxide coated copper during the thermal cycling test. The simulation results revealed that the cuprous oxide content in the copper substrate had a large effect on the adhesion between EMC and copper, which is consistent with the experimental observation. © 2005 IEEE.
ISSN 0569-5503
ISBN 0-7803-8906-9
Rights © 2005 IEEE. Personal use of this material is permitted. However, permission to reprint/republish this material for advertising or promotional purposes or for creating new collective works for resale or redistribution to servers or lists, or to reuse any copyrighted component of this work in other works must be obtained from the IEEE. This material is presented to ensure timely dissemination of scholarly and technical work. Copyright and all rights therein are retained by authors or by other copyright holders. All persons copying this information are expected to adhere to the terms and constraints invoked by each author's copyright. In most cases, these works may not be reposted without the explicit permission of the copyright holder.
Language English
Format Conference paper
Access View full-text via Scopus
View full-text via Web of Science
Files in this item:
File Description Size Format
01441438.pdf 322329 B Adobe PDF